ISO 8130-11:2019
2019-04
Тезис
This document specifies a comparative method for determining the flow characteristic of a fused thermosetting coating powder down a plane inclined at a set angle to the horizontal.
The aim of the test method described in this document gives an indication of the degree of melt flow that can occur during the curing of the coating powder. This characteristic contributes to the surface appearance and to the degree of coverage over sharp edges.
The test is a comparative method for checking for batch to batch variation in the behaviour of a given coating powder. Correlation between the results from coating powders of differing composition is not to be expected.
This method is not suitable for coating powders which have gel times of less than 1 min at the test temperature when characterised according to ISO 8130‑6. This method is also not suitable for textured powders.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2019-04Этап: Систематический пересмотр между-народного стандарта [90.20]
-
Версия: 2
-
Технический комитет :ISO/TC 35/SC 9ICS :87.040
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 8130-11:1997
-
Сейчас
ОпубликованоISO 8130-11:2019
Стандарт, который пересматривается каждые 5 лет
Этап: 90.20 (Hа стадии пересмотра)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)